+materials
+
+Alunimum
+   69 GPa tensile modulus, 110 MPa tensile strength
+   Misumi CAF5-2020-100
+   10x2x2 cm
+   $3.92 untapped, $7.87 tapped
+   0.0014, 0.0028 $/GPa/cm^3
+Garolite
+   8 GPa tensile modulus, 50 MPa tensile strength
+   McMaster 8491K26
+   24x36x1/4" $107
+   40 cm^3 = $1.20
+   0.0037 $/GPa/cm^3
+PLA
+   4 GPa tensile modulus, 60 MPa tensile strength
+   $20/kg
+   1.24 g/cm^3
+   40 cm^3 = $0.99
+   0.0061 $/GPa/cm^3
+HDPE
+   1 GPa tensile modulus, 20 MPa tensile strength
+   McMaster 8619K466
+   24x36x1/4" $39.01
+   40 cm^3 = $0.44
+   0.011 $/GPa/cm^3
+